Ultrasonically induced microemulsion polymerization of styrene

In this paper, ultrasonically induced microemulsion polymerization of styrene was successfully performed, possessing many merits such as high polymerization rate, the formation of small latex particles with a narrow size distribution, the absence of initiator and relatively low surfactant concentration. The monomer conversion reached 70% in 1 h, and the average diameter of polystyrene (PS) latex was about 30 nm which could be prepared with 3% surfactant (sodium dodecyl sulfate, SDS) concentration. The molecular weight of PS was around 106 and the poly-distribution index was 1.06, indicating a very narrow distribution. Several influencing factors were investigated in detail, showing that ultrasonically induced microemulsion polymerization is a new route to prepare PS nanoparticles.