Study on poly(oxybenzoate-p-trimethylene terephthalate) copolymer

This study examined copolymers synthesized from poly(trimethylene terephthalate) (PTT) and p-acetoxybenzoic acid using solution proton nuclear magnetic resonance (NMR) spectroscopy. Proton NMR spectra showed that these p-oxybenzoate (POB)/PTT copolyesters were almost random copolymers because the preference factor of POB bonded to another POB unit in these copolyesters is close to 1.0 with a POB content between 20 and 80 mol%. The melting and crystallization behaviors of these copolyesters were studied by differential scanning calorimetry (DSC). In the heating DSC scan of the POB rich composition, the endothermic peak is weaker because the enthalpy of fusion decreased due to a melting transition from a crystalline to anisotropy liquid state. Thermogravimetric analysis results indicated that the decomposition temperature (Td) increased with POB content. The crystalline morphology of the copolyester was further investigated with a polarized optical microscope, indicating that the POB/PTT copolyesters with 60 mol% POB are highly anisotropic in the liquid state.