Crystallization kinetics of poly(hexamethylene succinate)

Isothermal and nonisothermal crystallization kinetics of polyester 64 have been investigated by means of differential scanning calorimetry and optical microscopy. The Avrami analysis has been performed to obtain the kinetic parameters of primary crystallization. These indicate a three-dimensional spherulitic growth on heterogeneous nuclei for the isothermal crystallization, whereas an sporadic nucleation becomes dominant in the nonisothermal crystallization. The maximum crystallization rate of polyester 64 was deduced to take place at a temperature close to −3 °C. Polarizing light microscopy showed that spherulites with a negative birefringence are formed during isothermal crystallization, whereas transmission electron microscopy indicates that the b crystallographic axis is aligned parallel to the spherulitic radius.