Random copolymers of N-isopropylacrylamide and methacrylic acid monomers with hydrophobic spacers: pH-tunable temperature sensitive materials

Two series of random copolymers of N-isopropylacrylamide (NIPAAm) and comonomers derived from methacrylic acid with a different number of methylene units as hydrophobic spacers (n=4, 7 and 10) were synthesized via free radicals. The first series was prepared having the acid groups methoxy-protected while the second series have the acid groups free. The NIPAAm-copolymers of both series were prepared varying the comonomer content from 5 to 20 mol%. All the copolymers were characterized by FTIR, DSC, 1H NMR and SLS. The aqueous solution behaviour of the copolymers having methoxy-protected acid groups shows that the comonomer increases the hydrophobicity of the copolymer chain and decreases its lower critical solution temperature (LCST). For the copolymers having free acid groups, hydrogen-bonding is responsible for a further decrease in the LCST of these copolymers in pure water. In buffer solutions, every acid comonomer have a critical ionization degree (αcrit) above which the LCST increases with increasing comonomer content while at an ionization degree lower than αcrit the LCST decreases with increasing comonomer content. In dependence of comonomer content, number of methylene units in the spacer and the pH of the buffer solution, the LCST of the copolymers can be varied widely, showing that these random copolymers have pH-tunable temperature sensitivity.