Phase morphology, crystallisation behaviour and mechanical properties of isotactic polypropylene/high density polyethylene blends

The phase morphology, crystallisation behaviour and mechanical properties of isotactic polypropylene (iPP)/high density polyethylene (HDPE) blends were investigated. It was found that the properties are intimately related to each other. The morphology of the blends showed a two phase structure in which the minor phase was dispersed as domains in the major continuous matrix phase. The domain size of the dispersed phase increased with increasing concentration of that phase due to coalescence. It was also found that the domain size of the dispersed phase depends on the viscosity difference between the two phases. For a given HDPE/iPP blend, where HDPE is the matrix and iPP is the dispersed phase, the iPP domains were smaller than HDPE domains of the corresponding iPP/HDPE blend where iPP is the matrix and HDPE is the dispersed phase. A co-continuous morphology was observed at 50/50 PP/HDPE composition. Crystallinity studies revealed that blending has not much effect on the crystalline melting point of polypropylene and high density polyethylene. The crystallisation enthalpy and heat of fusion values of HDPE and PP in the blend were decreased as the amount of the other component increased. The variation in percent crystallinity of HDPE and PP in the blend was found to depend on the morphology of the blend. All the mechanical properties except Youngʹs modulus and hardness showed negative deviation from the additivity line. This is due to the incompatibility of these blends.