Synthesis, characterization and photocrosslinking properties of polyacrylamides having bromo substituted pendant cinnamoyl moieties

New 3- and 4-bromocinnamoyl aniline were synthesized condensing 4-aminoacetophenone and the respective bromobenzaldehydes in the presence of sodium hydroxide. The monomers, 4-(3′-bromocinnamoyl) phenyl acrylamide (4,3′-BCPA) and 4-(4′-bromocinnamoyl) phenyl acrylamide (4,4′-BCPA) were prepared by reacting the respective chalcones and acryloyl chloride in the presence of triethylamine at 0–5 °C. Homopolymers of 4,3′-BCPA and 4,4′-BCPA was carried out in methyl ethyl ketone using benzoyl peroxide (BPO) under nitrogen atmosphere at 70 °C. The prepared polymers were characterized by UV, IR, 1H-NMR and 13C-NMR techniques. The molecular weights (Mw and Mn) of the polymers were determined by gel permeation chromatography. The thermogravimetric analysis (TGA) of the polymers in nitrogen atmosphere reveals that they possess very good thermal stability required of a negative type photoresist. The glass transition temperature of poly(4,3′-BCPA) and poly (4,4′-BCPA) were found to be 55 and 64 °C respectively. The solubility of the polymers was tested in various polar and non-polar solvents. Photocrosslinking nature of the polymer samples was carried out in the presence and absence of various triplet photosensitizers in solution phase using chloroform solvent under medium frequency UV light. For using the polymers as negative photoresist materials the rate of photocrosslinking of the polymers was measured under the influence of different solvents, concentrations and position of the substituent.