Synthesis and properties of novel poly(amide-imide)s containing pendent diphenylamino groups

A new dicarboxylic acid, 2,4-bis(N-trimellitoyl)triphenylamine, bearing two preformed imide rings was synthesized from the condensation of 2,4-diaminotriphenylamine and trimellitic anhydride at 1:2 molar ratio. A series of poly(amide-imide)s (PAIs) with inherent viscosities of 0.38–0.66 dl/g were prepared by triphenyl phosphite-activated polycondensation from the diimide–dicarboxylic acid with various aromatic diamines. All the resulting PAIs were readily soluble in a variety of organic solvents and formed strong and tough films via solution casting. These PAIs have useful levels of thermal stability associated with moderately high glass-transition temperatures (259–314 °C) and 10% weight loss temperatures in excess of 530 °C in nitrogen or in air.