Synthesis of cationic core-shell latex particles

Surfactant-free seeded (core-shell) polymerization of cationic polymer colloids is presented. Polystyrene core particles with sizes between 200 nm and 500 nm were synthesized. The number average diameter of the colloidal core particles increased with increasing monomer concentration. Cationic shells were introduced by co-polymerizing styrene with the cationic monomers (vinylbenzyl)trimethylammonium chloride (VBTMAC), [(2-methacryloyloxy)ethyl] trimethylammonium chloride (METMAC) and [(2-(acryloyloxy)ethyl] trimethylammonium chloride (AETMAC) onto the polystyrene cores. The cationic monomer AETMAC, undocumented to our knowledge in colloid synthesis, produced the best cationic shells and could be incorporated at much higher concentrations in the shell compared to the commonly used VBTMAC and METMAC, which yielded undesired polyelectrolyte side products already at relatively low cationic monomer concentrations. In shell formation, feed concentrations of AETMAC between 1.3 mol% (2.4 wt%) and 10.7 mol% (20 wt%) in styrene could be employed, allowing us to control colloid surface charge density over a wide range. The influence of various polymerization parameters (initiator concentration, cross-linking agent, and ionic strength) on the co-polymerization process with AETMAC is discussed. Core-shell particles were characterized using HR-SEM, potentiometric titration and zeta potential measurements.