A new route to obtain PVDF/PANI conducting blends

Electrically conductive poly(vinylidene fluoride)(PVDF) – polyaniline blends of different composition were synthesized by chemical polymerization of aniline in a mixture of PVDF and dimethylformamide (DMF) and studied by electrical conductivity measurement, UV–Vis–NIR and FTIR spectroscopy. The samples were obtained as flexible films by pressing the powder at 180 °C for 5 min. The electrical conductivity showed a great dependence on the syntheses parameters. The higher value of the electrical conductivity was obtained for the oxidant/aniline molar ratio equal to 1 and p-toluenesulfonic acid–TSA/aniline ratio between 3 and 6. UV–Vis–NIR and FTIR spectra of the blend are similar to the doped PANI, indicating that the PANI is responsible for the high electrical conductivity of the blend. The electrical conductivity of blend proved to be stable as a function of temperature decreasing about one order at temperature of 100 °C. The route used to obtain the polymer blend showed to be a suitable alternative in order to obtain PVDF/PANI–TSA blends with high electrical conductivity.