Cure kinetics of epoxy–amine resins used in the restoration of works of art from glass or ceramic

The cure kinetics of two epoxy/amine resins, Araldite 2020 and AY103-HY956 widely used as adhesives in the restoration of works of art from glass or ceramic was investigated using FTIR spectroscopy. These resins are two-part adhesives, consisting of a resin – A, based on a diglycidyl ether of bisphenol A, and a hardener – B which is either a cycloaliphatic amine (isophorone diamine) for Araldite 2020, or a mixture of three aliphatic amines in HY956. The study was based on the collection of IR spectra, in the middle range (4000–600 cm−1), of mixtures of resin and hardener at different proportions and isothermal temperatures (22–70 °C) as a function of curing time. A kinetic model was employed to simulate the experimental data using two kinetic rate constants. Diffusion control was incorporated to describe the cure behaviour at high degrees of conversion. From fitting to experimental data the kinetic and diffusional parameters were estimated, together with the activation energies of the kinetic and autocatalytic rate constants. It was found that higher degrees of curing are obtained at higher temperatures and increased amounts of hardener. Differences in the performance of the two adhesives are explained based on the type of the amines used as hardener.