Preparation of composites and nanocomposites based on bentonite and poly(sodium acrylate). Effect of amount of bentonite on the swelling behaviour

A series of composite and nanocomposite hydrogels were synthesized by copolymerization reaction of partially neutralized acrylic acid (SA) on bentonite micropowder (BT) using N,N′-methylenebisacrylamide (MBA) as a crosslinker and potassium persulfate (I) as an initiator in aqueous solution. The influences of Na+-BT, organoBT (O-BT), and the content of the BT in the copolymeric gels on the swelling behaviour in deionized water and saline solution (0.2 wt.% NaCl(aq)) were investigated. Results showed that the equilibrium swelling (W∞) was decreased by adding a small amount of the BT, however, at higher BT contents, the W∞ increased with the increase of the amount of clay. It was found that a concentration of 14 wt.% Na+-BT gave the best results absorption (955 g/g). Moreover, the amount of swelling for these absorbents in saline solution was smaller than that in deionized water. These hydrogels were characterized by X-ray diffraction and scanning electron microscopy. Finally, the thermogravimetric analysis indicated that introduction of clay to the polymer network resulted in an increase in thermal stability.