Collagen-based highly porous hydrogel without any porogen: Synthesis and characteristics

In this contribution we have developed a collagen-based highly porous hydrogel by neutralizing the grafted poly(acrylamide-co-acrylic acid) after gel formation. Preparation of the hydrogels involved free radical polymerization of a combination of hydrolyzed collagen, acrylic acid (AA), acrylamide (AAm) and distilled water, in appropriate amounts and contained a crosslinking agent called N,N′-methylene bisacrylamide (MBA). The chemical structure of the hydrogels was characterized by means of FTIR spectroscopy, DSC and TGA thermal methods. Morphology of the samples was examined by scanning electron microscopy (SEM). Systematically, the certain variables of the graft copolymerization were optimized to achieve maximum swelling capacity. The absorbency under load (AUL) and centrifuge retention capacity (CRC) were measured. The swelling ratio in various salt solutions was also determined and additionally, the swelling of hydrogels was measured in solutions with pH ranged 1–13. The synthesized hydrogel exhibited a pH-responsiveness character so that a swelling-collapsing pulsatile behavior was recorded at pH 2 and 8.