Synthesis and characterization of new polyimides containing ethynylene linkages

We have synthesized a series of new diamines containing bis(ethynylaniline) linkages by bromine substitution reaction of ethynylaniline with 4,4′-bis(4-bromophthalimido)diphenylether (PODA) or 1,4-bis(4-bromophthalimido)benzene (PPDA). The intermediates were separated at each step, purified and characterized by the spectroscopic techniques. The model compound having imide and triple bond moiety was synthesized in order to elucidate the nature of the products formed from the ethynyl curing by FT-IR spectroscopy. The polymerization reaction of ethynylaniline diamines with various dianhydrides gave fully imidized and soluble aromatic polyimides. The thermally cured polyimide samples displayed good solvent resistance. The thermal crosslinking of triple bond moieties in the main chain was carried out by heating in the temperature range from 150 to 400 °C. The glass transition temperature of polyimide completely disappeared after heat treatment at 400 °C for 5 min. The polyimides derived from diamines containing bis(ethynylaniline) groups were thermally stable after heat treatment.