Mechanical properties and micro-structures of calcium aluminate based ultra high strength cement

This paper describes the mechanical properties and microstructure of calcium aluminate based ultra high strength cement at early age. By using silica fume, polycarboxylate based superplasticizers and a hybrid defoaming mixer, which is anon-contact mixer, cement paste with water to powder ratio of 0.1 can be cast in a mold. When the water to powder ratio is 0.1, the bending strength of hardened samples can be obtained over 30 MPa. Samples were cured at 40 or 60 °C for 7 days. At 60 °C, C3AH6 is mainly produced, whereas C3AH6 and C2AH8 are produced at 40 °C. The mechanical properties of hardened samples with low water to powder ratio are related to the pore volume and pore size distribution.