Synthesis and crystallization behaviors of poly(styrene-b-isoprene-b-ε-caprolactone) triblock copolymers

The triblock copolymers, poly(styrene-b-isoprene-b-ε-caprolactone)s (PS-b-PI-b-PCL) have been synthesized successfully by combination of anionic polymerization and ring-opening polymerization. Diblock copolymer capped with hydroxyl group, PS-b-PI-OH was synthesized by sequential anionic polymerization of styrene and isoprene and following end-capping reaction of EO, and then it was used as macro initiator in the ring-opening polymerization of CL. The results of DSC and WAXD show big effect of amorphous PS-b-PI on the thermal behaviors of PCL block in the triblock copolymers and the lower degree of crystalline in the triblock copolymer with higher molecular weight of PS-b-PI was observed. The real-time observation on the polarized optical microscopy shows the spherulite growth rates of PCL27, PCL328 and PS-b-PI-b-PCL344 are 0.71, 0.46 and 0.07 μm s−1, respectively. The atomic force microscopy (AFM) images of the PS90-b-PI66-b-PCL28 show the columns morphology formed by it’s self-assembling.