Studies on the blends of cardanol-based epoxidized novolac resin and CTPB

Cardanol-based novolac-type phenolic resins were synthesized with different mole ratios of cardanol-to-formaldehyde, viz., 1:0.6, 1:0.7, and 1:0.8. These novolac resins were epoxidized with molar excess of epichlorohydrin at 120 °C in basic medium. The epoxidized novolac resins were, separately, blended with different weight ratios of carboxyl-terminated polybutadiene liquid rubber ranging between 0–25 wt% with an interval of 5 wt%. All the blends were cured at 150 °C with 40 wt% polyamide. The formation of various products during the curing of blend samples has been studied by Fourier-transform infra-red spectroscopic analysis. The tensile strength and elongation-at-break of the cured samples increased up to 15 wt% in the blend and decreased thereafter. This blend sample was also found to be most thermally stable system. The blend morphology, studied by scanning electron microscopy analysis, was finally correlated with the structural and property changes in the blends.