Comparative study of photoelectric properties of a copolymer and the corresponding homopolymers based on poly(3-alkylthiophene)s

As semiconducting materials in organic light-emitting devices (OLEDs), a novel, highly soluble poly[(3-octylthiophene)-co-(3-(2-ethyl-1-hexylthiophene))] (P3OTIOT) and the corresponding homopolymers (poly(3-octylthiophene) (P3OT) and poly(3-isooctylthiophene) (P3IOT)) were prepared by an FeCl3-oxidative approach to compare their photoelectric properties. Characterization of the polymers included FT-IR, 1H NMR, gel permeation chromatography (GPC), thermo-gravimetric analysis (TGA), UV–vis spectroscopy, photoluminescence (PL) and electroluminescence (EL). P3OTIOT and P3OT depicted excellent solubility in common organic solvents. TGA studies showed that all of the materials exhibited very good thermal stabilities, losing 5% of their weight on heating to 300 °C. The optical property investigations showed that the band-gap energy of P3OTIOT was similar to that of P3OT (2.43 eV) at 2.45 eV and 6% lower than that of P3IOT (2.6 eV) in CHCl3 solution. In PL spectra, the emission maxima of P3OTIOT and P3IOT were 50 nm and 130 nm blue-shifted with respect to that of P3OT, respectively. However, the PL intensity of P3OTIOT was seven times higher than that of P3OT. Single layer polymer light-emitting devices (PLEDs) with the ITO/polymer/Ag configurations were fabricated by the spin-coating method with P3OT, P3IOT and P3OTIOT as the EL materials, which exhibited red (650 nm), orange-red (610 nm) and yellow-green (525 nm) EL, respectively. The external EL quantum efficiencies (QE) of P3IOT and P3OTIOT devices are 6.4 × 10−3% and 5.1 × 10−3% which are about five and four times higher than that of the P3OT device (1.2 × 10−3%), respectively. The turn-on voltage of the P3OTIOT device (5 V) is between that of the P3OT (4.5 V) and P3IOT (6 V) devices. These results indicated that the P3OTIOT combined the photoelectric properties of P3OT and P3IOT with excellent solubility, processability, low band-gap energy, high QE and low turn-on voltage in the PLEDs, and they might be excellent polymeric materials for applications in organic light-emitting diodes, light-emitting electrochemical cells and polymer solar cells.