Polyaniline/thermoplastic polyurethane blends: Preparation and evaluation of electrical conductivity

Conducting polymer blends whose undiluted components have different properties are promising materials for specific applications and have attracted interest in recent years. The aim of this study was to obtain and evaluate the electrical conductivity of polyaniline doped with dodecylbenzenesulfonic acid (PAni.DBSA)/polyurethane thermoplastic (TPU) blends. The PAni.DBSA was synthesized from DBSA-aniline (DBSAn) salt through an emulsion polymerization in tetrahydrofurane (THF) or in the presence of polyurethane thermoplastic solution, resulting in pure PAni.DBSA or PAni.DBSA/TPU blends. Blends of PAni.DBSA/TPU were also prepared through casting, at room temperature, after dissolving both components in THF as a common solvent. The insulator–conductor transition was very sharp and the percolation threshold was lower than 2.7 wt% of PAni.DBSA. The electrical conductivity of PAni.DBSA/TPU blends, prepared by both methods, reached maximum values at a PAni.DBSA concentration of 40 wt%, close to the value observed for the undiluted conducting polymer. However, for a PAni.DBSA content lower than 30 wt%, the electrical conductivity was dependent on the blend preparation method. Blends were characterized by infrared spectroscopy, thermogravimetric analysis (TG) and optical microscopy. The electrical conducting characteristics of the PAni.DBSA/TPU blends prepared using different procedures indicate a high potential for their successful application in electrical processes.