Synthesis and chelation properties of new polymeric ligand derived from 8-hydroxy-5-azoquinoline hydroxy benzene

8-Hydroxy-5-azoquinoline phenyl methacrylate-formaldehyde (8H5AQPMA-F) macromonomer was prepared from methacryloyl chloride with condensation products of 8-hydroxy-5-azoquinoline phenol-formaldehyde, and polymerized in DMF at 70 °C using benzoyl peroxide as free radical initiator. Poly(8H5AQPMA-F) was characterized by infrared and nuclear magnetic resonance spectroscopic techniques. Polychelates were obtained when the DMF solution of the resin containing few drops of ammonia was treated with the aqueous solution of Cu(II)/Ni(II). Elemental analysis of the polychelates indicates that the metal to ligand ratio was about 1:2. The IR spectra of polychelates suggest that the metals were coordinated through the oxygen of the phenolic-OH group and nitrogen of the quinoline ligand. The DRS and magnetic moment data indicate a square planar for Cu(II) complex whereas octahedral for Ni(II) complex. The TGA data revealed the thermal stability of the resin and the polychelates. X-ray diffraction study revealed the incorporation of the metal ions significantly enhanced the degree of crystallinity. The sorption properties of the chelate-forming resin towards various divalent metal ions [Cu(II) and Ni(II)] were studied as a function of pH and electrolyte.