Synthesis of crosslinkable ABA triblock copolymers based on allyl methacrylate by atom transfer radical polymerization

Copper(I)-mediated living radical polymerization was used to synthesize a series of self-crosslinkable ABA triblock copolymers in which the side blocks are formed by a monomer supporting a reactive functional group, as allyl methacrylate (AMA). The copolymers were prepared according with a two steps synthetic methodology. In the first step, α,ω-dibromo homopolymers of polystyrene (PS), poly(methyl methacrylate) (PMMA) and poly(butyl acrylate) (PBA) were synthesized by atom transfer radical polymerization (ATRP). In the second step, these telechelic polymers were employed as macroinitiators for the ATRP of AMA in benzonitrile solution at 70 °C with CuCl/N,N,N′,N″,N″-pentamethyldiethylenetriamine (PMDETA) as catalyst system in order to obtain well-defined functionalized triblock copolymers. The living nature of the block copolymerizations involved was investigated in each case and a similar general behaviour was found. Thus, the molecular weights increased fairly linearly with the conversion degree with first-order kinetics in respect of monomer until moderate conversions, where secondary reactions become more relevant. Finally, intermacromolecular crosslinking were observed giving macrogels as a unique reaction product. The polymers were characterized by different characterization techniques, such as size exclusion chromatography (SEC), 1H NMR spectroscopy and differential scanning calorimetry (DSC). In addition, the facile thermal crosslinking of these block copolymers was evaluated from rheological measurements.