Synthesis of new polyazines by 1,4 photochemical or anionic polymerization of 1,2-diaza-1,3-butadienes

Photochemical and anionic polymerizations of 1,2-diaza-1,3-butadienes are described. Photochemical polymerization was smoothly performed by irradiation of some 1-aminocarbonyl-1,2-diaza-1,3-butadienes with high pressure mercury arc (λ = 300 nm) in the presence of allyltributylstannane. Molecular weights (Mw) in the range 14.6–559 × 102 g/mol were obtained. The TGA curve revealed a first weight loss starting at about 200 °C of some 85%, and a second starting at about 300 °C. The DSC showed the glass transition (Tg) at about −34 °C. Anionic polymerization was performed by treatment of some 1-alkoxycarbonyl-1,2-diaza-1,3-butadienes with n-butyllithium. Molecular weights (Mw) in the range 8.44–242 × 102 g/mol were obtained.