Modelling physical properties of highly crystallized polyester reinforced with multiwalled carbon nanotubes

The effects of carbon nanotubes dispersion into thermoplastic polymers are complex and strongly dependent upon their aggregation state. A poly(ethylene terephthalate) (PET) matrix has been reinforced through addition of multiwalled carbon nanotubes (MWCNTs). Such an addition has generated an increase in flexural modulus and a decrease in flexural strength at room temperature, and an increase in both properties above the glass transition temperature (at 100 °C). These different behaviours, dictated by temperature, have been investigated through two different micromechanical models that have permitted to put forward hypothesis on failure mechanisms and to shed light on the role played by crystalline phase. The results of thermal analyses have shown that the heat capacity of PET nanocomposites varies according to the MWCNTs content as the flexural modulus. Such a similarity has suggested to modify the Halpin-Tsai equations (H-T), typically used to predict elastic properties of short fibres reinforced composites, in order to determine the relationships occurring between PET specific heat and aspect ratio of dispersed MWCNT. The analyses performed by means of either classical H-T (elastic modulus) or modified H-T (heat capacity) equations, provided very similar estimation of the MWCNT aspect ratios. In addition, a simple elaboration of the modified H-T equations permitted the calculation of rigid amorphous fraction (RAF) into PET. The obtained values were slightly higher than those evaluated by means of a procedure based on the loss tangent peak variation measured through dynamic mechanical experiments. The detected strength decrease at 25 °C have been attributed to crack propagation through a percolative path between crystalline coating layer of MWCNTs and PET (favoured by matrix brittleness), while at 100 °C the crack propagation is hampered by rubbery behaviour of the matrix.