Industrial Atmospheric Corrosion Resistance of P-RE Weathering Steel Original Research Article

The corrosion behavior of low-carbon steel (CS), P-bearing steel (PS) and P-RE weathering steel (P-REWS) exposed for two years in Jiangjin of China was investigated. The results showed that during 2-year exposure test, corrosion data of the experimental steels followed the bilogarithmic equation, and the average corrosion depth of PS and P-REWS was decreased by 19.5% and 28.2% respectively compared with that of CS. Scanning electron microscope, electrochemical impedance spectroscope and Fourier transform infrared spectroscope were used to characterize the corrosion products. The research results showed that P in steel could promote the formation of an amorphous ferric oxyhydroxide layer near the substrate. The addition of RE could effectively increase the charge transportation resistance of rust.