Structural characterization and corrosive property of Ni-P/CeO2 composite coating

Electroless Ni-P/nano-CeO2 composite coating was prepared in acidic condition, and its microstructure and corrosive property were compared with its CeO2-free counterpart. Scanning electronic microscopy (SEM), transmission electronic microscopy (TEM), X-ray diffraction spectrometer (XRD), and differential scanning calorimeter (DSC) were used to examine surface morphology and microstructure of the coating. Corrosive investigation was carried out in 3%NaCl+5%H2SO4 solution. The results showed that Ni-P coating had partial amorphous structure mixed with nanocrystals, whereas the Ni-P/CeO2 coating had perfect amorphous structure. In high temperature condition, Ni3P precipitation and Ni crystallization occurred in both coatings but at different temperatures, whereas the Ni-P/CeO2 coating had sintered phase of NiCe2O4 spinels. The anticorrosion property and passivity were improved in the CeO2-containing coating due to its less liability to undergo local-cell corrosion than its CeO2-free counterpart. During the co-deposition process, some Cen+ (n=3, 4) ions may be adsorbed to the metal/solution interface, hinder nickelʹs crystal-typed deposition and promote phosphorous deposition. The nano-CeO2 doping finally resulted in the coatingʹ perfect amorphous structure and good anti-corrosive property.