Visible-light absorption and photocatalytic activity of Cr-doped TiO2 nanocrystal films

Chromium doped titanium dioxide (TiO2) nanocrystal films with various doping concentration have been successfully prepared by a sol–gel dip-coating process. These films have been characterized by XRD, XPS, AFM, and UV–vis absorption spectroscopy. It is found that Cr doping can effectively reduce the transition temperature of anatase to rutile phase as well as the grain size. The absorption edges of TiO2 thin films shift towards longer wavelengths (i.e. red shifted) from 375 nm to about 800 nm with increasing Cr concentration, which greatly enhances TiO2 nano-materials on the absorption of solar spectrum. The appearance of UV–vis absorption features in the visible region can be ascribed to the newly formed energy levels such as Cr 2p level and oxygen vacancy state between the valence and the conduction bands in the TiO2 band structure. The enhancement of the photocatalytic properties is observed for Cr-doped TiO2 thin film.