Observations on shear plug formation in Weldox 460 E steel plates impacted by blunt-nosed projectiles

Shear plug formation in circular Weldox 460 E steel plates impacted by blunt-nosed cylindrical projectiles with striking velocities between 100 and 500 m/s has been investigated. Target thickness and projectile impact velocity were the primary variables, and for each target thickness the ballistic limit curve of the material was precisely determined. The test at an impact velocity just below the ballistic limit for each target thickness was selected for a microscopic examination of shear localisation and fracture. In these tests, the plug was pushed only partway through the target, and the localised shear zones outlining the fracture were easily recognised both in the optical and scanning electron microscope. Clear evidence of adiabatic shear bands and material damage due to void growth was found in several of the target plates. Analytical models available in the literature were compared with the results from the experimental and microscopic studies. Reasonable agreement was found between calculations and experiments.