Luminescence and EPR studies of Eu2+ doped BaAl12O19 blue light emitting phosphors

Europium doped BaAl12O19 powder phosphors have been synthesized by combustion process within few minutes. The phosphors have been characterized by XRD, SEM, FT-IR, EPR and PL techniques. The EPR spectrum exhibits an intense resonance signal at g=1.96 characteristic of Eu2+ ions. In addition to this two weak resonance signals have been observed at g=2.28 and g=4.86. The population of the spin levels (N) for the resonance signal at g=1.96 is calculated as a function of temperature. By post-treating the phosphor at 1350 °C under a reducing atmosphere, it is observed that the population of spin levels has been increased five times. The excitation spectrum shows a peak at 326 nm with a shoulder at 290 nm. Upon excitation at 326 nm, the emission spectrum exhibits a well defined broad band with maximum at 444 nm emitting a blue light corresponding to 4f65d→4f7 transition. The luminescence intensity also has been enhanced to 60% by post-treating the phosphor at 1350 °C under a reducing atmosphere.