Growth, thermal and spectroscopic characterizations of BaNd2(MoO4)4 crystal

A new crystal, BaNd2(MoO4)4, has been grown from the flux melt based on Li2Mo3O10 by a spontaneous nucleation method. The phase structure of the obtained crystals was determined by X-ray powder diffraction. The result shows that the as-grown crystals are well crystallized and indexed in a monoclinic crystal system with space group B2/b. The specific heat of BaNd2(MoO4)4 crystal at 20 °C is 0.485 J/g K. Absorption and fluorescence spectra were also measured at room temperature. There are several strong and broad absorption peaks from 200 to 1200 nm and three emission transition bands located at 890, 1060, and 1334 nm are detected.