Luminescent sensitization and blue shift emission of Ir(ppy)2(VPHD) by copolymerization with MMA

Ir(ppy)2(VPHD) (ppy=2-phenyl pyridine, VPHD=6-(4-vinylphenyl)-2,4-hexanedione) was copolymerized with methyl methacrylate (MMA). The copolymer had high quantum yield of 52.3±0.5% in dilute ethyl acetate solution, and the yield increased around 45% than that of the iridium monomer. The maximum emission peaks for the copolymers shifted from 515 to 489 nm while the iridium complex content was less than 0.005 mol% in the feed. The blue emission at 489 nm and the green emission at 520 nm were analyzed by Lorenz function. They are attributed to 1MLCT and 3MLCT emissions, respectively.