Thermoluminescence characteristics of inorganically and organically capped ZnS:Cu nanophosphors

ZnS:Cu nanophosphors were prepared by wet chemical methods and characterized by X-ray diffraction (XRD). The typical morphologies of the nanophosphors were investigated by scanning electron microscopy (SEM). The thermoluminescence (TL) properties of inorganically and organically passivated ZnS:Cu nanophosphors were investigated after γ-irradiation using a 60Co source at room temperature. The TL glow curve of capped ZnS:Cu showed variation in TL peak and intensity as the capping agent was changed. Amongst the synthesized samples the TL glow curve of SiO2 capped ZnS:Cu showed the highest TL intensity. It has been found that TL response of SiO2 capped ZnS:Cu is linear in the range 10–550 Gy. A discussion of the obtained results is also presented.