Thermoluminescence and dosimetric aspects of topaz from Yono Shigar mine in Pakistan

Topaz shows thermoluminescence (TL) on heating after exposure to ionising radiation. A study was carried out to explore the possibility to design and develop a TLD (thermoluminescence dosimeter) from locally occurring topaz. Topaz was collected from a mine in Yono Shigar valley in northern Pakistan. The samples were identified as topaz by neutron irradiation, X-ray diffraction and X-ray fluorescence. The crystals of topaz were cut into chips of dimensions compatible to the commercial TLD readers. The chips were exposed to 60Co and/or 137Cs gamma irradiators. The investigation features included glow curve, dose and energy responses, sensitivity, fading, reproducibility and mechanical stability. The TL glow curves revealed a stable peak at about 250 °C, whose height rose linearly with increase of irradiation dose. The TL response versus dose (calibration curve) showed the linear behaviour between 10−2 and 102 Gy. The dose response was independent of gamma energies of 60Co and 137Cs. The response of topaz chips remained constant within 10% deviation from the initial value after 30 cycles of reuse. The rate of fading of topaz was very fast just after irradiation and slowed after a few days. Mechanical stability of the chips remained constant during handling in all investigation experiments. The topaz from Yono Shigar mine may be recommended as a TLD for gamma dose within 10−2–102 Gy.