Synthesis and study of optical and thermal properties of Mn doped CdS nanoparticles using polyvinylpyrrolidone

High quality and monodispersed CdS:Mn (1–5%) nanoparticles were synthesized by chemical precipitation method using PVP as surfactant. The structure and morphology of the CdS:Mn were investigated by means of XRD, FT-IR, TEM, UV–visible, PL, EPR and TG-DTA. XRD study was confirmed the formation cubic structured CdS:Mn nanoparticles. The optical absorption of Mn doped CdS nanoparticles was found to be 420–432 nm, which is significantly decreased from the bulk CdS material. Photoluminescence spectroscopy of the CdS:Mn nanocrystals showed a strong emission peak at 535 nm near the band edge along with a week green emission around 575 nm. The PL property of annealed (255 °C–850 °C) samples was also investigated under different excitations. The presence of PVP on the CdS:Mn surface and incorporated the Mn ion into CdS lattice were identified by FT-IR and EPR spectroscopy, respectively. TEM result showed spherical with monodispersed particles with typical size of 3.8–4.3 nm, which is a favorable characteristic for many applications. The major weight loss and gain were found in the thermogravimetric analysis (TGA) which corresponds to the decomposition and oxidation of the samples.