Author/Authors :
H.S Tripathi، نويسنده , , B. Mukherjee، نويسنده , , S. Das، نويسنده , , M.K. Haldar، نويسنده , , S.K. Das، نويسنده , , A. Ghosh، نويسنده ,
Abstract :
Stoichiometric magnesium aluminate spinel was synthesized by reaction sintering of alumina with caustic and sintered magnesia. The volume expansion of 5–7% during MgAl2O4 formation was utilized to identify the starting temperature of spinel formation and densification by high temperature dilatometry. The magnesia reactivity was determined by measurement of crystallite size and specific surface area. Caustic magnesia and sintered magnesia behave differently vis-à-vis phase formation and densification of spinel. Densification of stoichiometric Mag-Al spinel was carried out between 1650 and 1750 °C. Attempts were made to correlate the MgO reactivity with microstructure and densification of spinel.
Keywords :
D. Spinels , E. Refractories , C. Thermal expansion , A. Grain growth