Recycling of CRT panel glass as fluxing agent in the porcelain stoneware tile production

In the present work, the feasibility to substitute feldspar raw material in a porcelain stoneware body with Panel Cathode Ray Tube (CRT) glass was investigated. A standard batch and a composition, where 35 wt.% Na-feldspar was substituted by CRT glass, were sintered at different temperatures in the range of 1000–1250 °C. The degree of the densification was studied by evaluation of the closed and total porosity, while the sintering rate was estimated by non-isothermal dilatometric measures. The variation of the crystalline phase composition was evaluated by XRD analysis. From the preliminary study other ceramic samples with different percentages of CRT glass (i.e. 2.5, 5 and 10 wt.%) were prepared and fired in industrial kiln. The sintering parameters, the microstructure and the mechanical properties were measured and compared with the standard composition.