Preparation, structural and thermo-mechanical properties of lithium aluminum silicate glass–ceramics

Lithium aluminum silicate glasses of composition (wt%) 12.6Li2O–71.7SiO2–5.1Al2O3–4.9K2O–3.2B2O3–2.5P2O5 were prepared by the melt quench technique. These glasses were converted to glass–ceramics based on DTA data. X-ray diffraction (XRD) and Fourier transform infra-red spectroscopy (FTIR) were used to discern the phases evolved in the glass–ceramics. Phase morphology was studied using scanning electron microscopy (SEM). Thermal expansion coefficient (TEC) and glass transition temperature (Tg) of all samples were measured using thermo-mechanical analyzer (TMA). It was found that 3 h dwell time at crystallization temperature yielded samples with good crystallinity with a TEC of 9.461 × 10−6 °C−1. Glass–ceramic-to-metal compressive seal with SS-304 was fabricated using LAS glass–ceramic. The presence of metal housing and compressive stresses at the glass–ceramic-to-metal interface reduced average grain size and changed the overall microstructure.