Fabrication and thermal conductivity of AlN/BN ceramics by spark plasma sintering

Aluminum nitride/boron nitride (AlN/BN) ceramics with 15–30 vol.% BN as secondary phase were fabricated by spark plasma sintering (SPS), using Yttrium oxide (Y2O3) as sintering aid. Effects of Y2O3 content and the SPS temperature on the density, phase composition, microstructure and thermal conductivity of the ceramics were investigated. The results revealed that with increasing the amount of starting Y2O3 in AlN/BN, Yttrium-contained compounds were significantly removed after SPS process, which caused decreasing of the residual grain boundary phase in the sintered samples. As a result, thermal conductivity of AlN/BN ceramics was remarkably improved. By addition of Y2O3 content from 3 wt.% to 8 wt.% into AlN/15 vol.% BN ceramics, the thermal conductivity increased from 110 W/m K to 141 W/m K.