Transparent semiconductor zinc oxide thin films deposited on glass substrates by sol–gel process

Transparent semiconductor ZnO thin films were spin-coated onto alkali-free glass substrates by a sol–gel process. The influence of ZnO sols synthesized via different solvents (2-ME, EtOH or IPA) on the surface morphologies, microstructures, optical properties and resistivities of the obtained films were investigated. The as-coated films were annealed in ambient air at 500 °C for 1 h. X-ray diffraction results showed all polycrystalline ZnO thin films to have preferred orientation along the (0 0 2) plane. The surface morphologies, optical transmittances and resistivity values of the sol–gel derived ZnO thin films depended on the solvent used. The ZnO thin films synthesized with IPA as the solvent exhibited the highest average transmittance 92.2%, an RMS roughness of 4.52 nm and a resistivity of 1.5 × 105 Ω cm.