Physico-chemical investigation on mixed alkali metal ferrites prepared by solution combustion method – A comparative study

Mixed alkali metal nanoferrites of the compositions M0.5−X/2ZnXMn0.05Fe2.45−X/2O4 (M = Li, Na and K), where x varies from 0→0.5 in steps of 0.1, have been prepared by solution combustion method. Powder X-ray diffraction analysis for all the samples show the formation of single phase cubic spinel structure. The lattice parameter increases linearly with Zn content, which is attributed to ionic size differences of the cations involved. Both X-ray as well as experimental densities show upward trend with increasing ‘x’ due to increase in the molecular weight of the ferrite composition. Mössbauer spectra display the superimposition of paramagnetic doublet over ferrimagnetic sextet with increasing diamagnetic ‘Zn’ content. The key magnetic properties of the ferrite obtained, such as saturation magnetization and Curie temperature have also been studied. The combustion method used for the synthesis is a rapid approach for direct conversion of the stoichiometric reactant solutions into fine nanoparticles of ferrite product at a temperature (600 °C) much lower than that of the conventional ceramic method. Scanning electron micrographs confirm the formation of nanosized ferrites.