Alumina porous nanomaterials obtained by colloidal processing using d-fructose as dispersant and porosity promoter

Recently, great effort has been devoted to obtain porous materials with customized pore size distribution, high surface area and submicrometer sized microstructures or nanostructures. In this work, the viability of colloidal processing routes to obtain porous bulk ceramics using alumina nanopowders and d-fructose as a dispersant and a porosity former has been explored. The rheological behaviour of nanosuspensions was studied in order to assure their stability and to analyse the influence of different parameters (solids loading, fructose content, pH, sonication time). Mesoporous green bodies were obtained by slip casting with d-fructose in concentrations ranging from 5 to 50 wt%. The drying and burning-out conditions were determined by DTA-TG measurements and the sintering cycles were selected from the dynamic sintering curve. Sintered alumina materials with high porosity (>60%), open microstructures, submicrometer sized porosity (dp = 140–210 nm) and grain size lower than 500 nm, were obtained for pieces sintered at temperatures of 1300 and 1400 °C. The influence of different processing parameters on the porosity and the microstructure of the sintered materials is discussed.