Influence of powder size on characteristics of air plasma sprayed silicon coatings

Silicon powders with different medium sizes (114 μm, 79 μm and 31 μm, respectively) were used to fabricate coatings by air plasma spraying. The velocity and temperature of in-flight silicon particles during plasma spraying were determined. The composition and microstructure of the coatings were characterized and some physical properties of the coatings were measured. The obtained results showed that the size of silicon particles had great influence on their velocity and temperature in plasma flame. The oxidation of silicon particles in the spraying process was observed and is higher for particles of smaller sizes. Areas of silicon oxide in micrometer size are embedded and randomly distributed in the coating. The surface roughness and void content of silicon coatings increase with an increase in the particle size of the powders. The microhardness and oxygen content of coatings decrease with an increase in the particle size. However, the size of silicon particles has little impact on the deposition efficiency of silicon under the same deposition conditions.