Effect of composition variation on phases and photoluminescence properties of β-SiAlON:Ce3+ phosphor

Ce3+-doped β-SiAlON blue phosphors with composition of CexSi6−zAlzOzN8−z (0.2≤z≤4) at a fixed x=0.01 were synthesized by the gas pressure sintering method. The phases and photoluminescence properties were found to be directly correlated to the z value. Higher z value would result in the formation of AlN polytypoid impurity phases. The optimal z value resides in the range 0.3≤z≤0.5, by which high purity of β-SiAlON phase, good crystallinity and fine grain size were obtained, leading to the best luminescence properties. These phosphors could be a good candidate for application in white light-emitting diodes using InGaN-based near–ultraviolet chips.