Electrochemical and structural study of Ce0.8Sm0.2−xLaxO1.9 electrolyte materials for SOFC

Ce0.8Sm0.2−xLaxO1.9 powders, denoted as LaxSDC (for x=0, 0.01, 0.03, 0.05, 0.07 and 0.1), were synthesized via the mechanical milling reaction method. The La3+ doping content has a remarkable influence on structural and electrical properties. The phase identification and morphology were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Lattice parameters were calculated by the Rietveld method. It was observed that the lattice parameter values in Ce0.8Sm0.2−xLaxO1.9 systems obey Vegardʹs law. The pellets were then sintered at 1500 °C in air for 7 h. The relative densities of these pellets were over 93.7%.The electrical conductivity was studied using two-probe impedance spectroscopy and results showed that the conductivity of Ce0.8Sm0.2−xLaxO1.9 first increased and then decreased with La dopant content x. Results also showed that Ce0.8Sm0.17La0.03O1.9 had the highest electrical conductivity, σ700 °C equal to 3.8×10−2 Scm−1 and an activation energy equal to 0.77 eV. It was therefore concluded that co-doping with the appropriate amount of La can further improve the electrical properties of ceria electrolytes.