High energy-storage properties of [(Bi1/2Na1/2)0.94 Ba0.06] La(1−x) ZrxTiO3 lead-free anti-ferroelectric ceramics

Energy-storage properties of [(Bi1/2Na1/2)0.94Ba0.06]La(1−x)ZrxTiO3 (BNT-BLZT, x=0, 0.02, 0.04, and 0.06) lead-free anti-ferroelectric ceramics fabricated via the conventional sintering technique were first investigated. Calculation from the X-ray diffraction results reveals that BNT-BLZT ceramic possesses a single perovskite structure phase. In addition, the P–E hysteresis loops measured at room temperature show that the BNT-BLZT (x=0.02) ceramics obtain the maximum P value of 37.5 μC/cm2 and the largest energy-storage density Wmax is 1.58 J/cm3. The temperature dependence of dielectric permittivity εr and dielectric loss tanδ illustrate that the addition of Zr can improve the piezoelectric properties of BT-BLZT ceramics. These properties indicate that BNT-BLZT ceramics might be a promising lead-free anti-ferroelectric material for energy storage application.