Characterization of La0.58Sr0.4Co0.2Fe0.8O3−δ–Ce0.8Gd0.2O2 composite cathode for intermediate temperature solid oxide fuel cells

La0.58Sr0.4Co0.2Fe0.8O3−δ–Ce0.8Gd0.2O2 (LSCF–GDC) composite cathodes with various weight ratios 90%, 70% and 50% of LSCF were prepared. Mechanical properties, thermal expansion properties and electrical properties were measured for potential applications in solid oxide fuel cells (SOFCs) with graded cathodes. LSCF and GDC as pure cathode and electrolyte materials were characterized as reference. The absence of new phases as confirmed by X-ray diffraction (XRD) analysis demonstrated the excellent compatibility between the cathode and electrolyte materials. Mechanical properties such as hardness and fracture toughness were measured by the micro-indentation technique, while hardness and elastic modulus were measured by the nano-indentation technique. Thermal expansion behavior was recorded by a dilatometer. Electrical conductivity was measured by the four probe DC method. The 50% LSCF–GDC composite has the lowest relative density among all the samples. Thermal expansion coefficients (TECs) and electrical conductivity increased with addition of LSCF contents in the composite, while mechanical properties depended more on the density than the LSCF content.