Phase transition behavior and temperature-stable piezoelectric properties of new quaternary (K, Na)NbO3 based ceramics

(K, Na)NbO3-based lead free materials have been found to exhibit good piezoelectric properties due to the orthorhombic–tetragonal polymorphic phase transition (PPT) temperature compositionally shifted downward to near room temperature. However, this transition correspondingly results in a strong temperature dependence of the dielectric and piezoelectric properties. In this work, new quaternary (1−x) (K0.4425Na0.52Li0.0375)(Nb0.8925Sb0.07Ta0.0375)O3 (KNLNST)–xSrTiO3 (ST) lead-free piezoelectric ceramics were fabricated by a conventional ceramic technique and their structure and piezoelectric properties were also studied. The results of X-ray diffraction reveal that SrTiO3 diffuses into the KNLNST lattices to form a new solid solution with a perovskite structure. After the addition of SrTiO3, tetragonal–orthorhombic phase transition shifts to lower temperatures. The good piezoelectric properties of 0.995 KNLNST–0.005 ST material were found to be d33∼295 pC/N, kp∼42%, and εr∼1902, with greatly improved temperature stability over the temperature range of 0–100 °C, demonstrating practical potential for actuator and ultrasonic transducer applications.