Hailong Wang، نويسنده , , Chih-Lun Feng، نويسنده , , Sea-Hoon Lee، نويسنده , , Jianbao Chen، نويسنده , , Bingbing Fan، نويسنده , , DELIANG CHEN ، نويسنده , , Hongxia Lu، نويسنده , , Hongliang Xu، نويسنده , , Rui Zhang، نويسنده ,
Abstract :
Al3BC3 was fabricated by in-situ reaction of Al, B4C and activated carbon additives, which improved both sinterability and mechanical properties of the ZrB2 ceramics. The densification of ZrB2 was nearly completed at 1700° C using spark plasma sintering (SPS). Both fracture toughness and flexural strength of ZrB2 ceramics increased with the content of sintering additives, which respectively reached a maximum of 6.17 MPa m1/2 and 529 MPa at 15 wt% ABC content.