Facile synthesis of CdS nanoparticles photocatalyst with high performance

A simple one-step solid-state reaction has been introduced to synthesize CdS nanoparticles. The as-prepared CdS product was characterized by X-ray powder diffraction (XRD), BET surface area measurement, field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), particle size distribution (PSD) and UV–vis absorption spectrum. The experiment results reveal that the CdS product was composed of nanoparticles about 60 nm in diameter, of which specific surface area is 78.02 m2/g. The photocatalysis results indicate that the CdS nanoparticles exhibit excellent photocatalytic activity for the degradation of rhodamine B under UV irradiation. Nearly 95% of rhodamine B was degraded after 60 min of irradiation, higher than that of P25, which is due to the large specific surface area and mesoporous structure.