Effects of sintering temperature and poling conditions on the electrical properties of Ba0.70Ca0.30TiO3 diphasic piezoelectric ceramics

The effects of sintering temperature and poling conditions on the electrical properties of tetragonal and orthorhombic diphasic Ba0.70Ca0.30TiO3 (BCT) lead-free ceramics have been systematically investigated. On the one hand, with increasing sintering temperature from 1270 °C to 1400 °C, the bulk density increases monotonically and the Curie temperature keeps almost constant with the value of ∼120 °C, whereas the grain size, the maximum relative dielectric constant, room temperature polarization reach the maximum values for samples sintered at 1340 °C. On the other hand, it is found that the piezoelectric property depends on poling electric field and poling temperature significantly. An enhanced piezoelectric behavior of d33=126 pC/N, kp=0.29, and Qm=588 is obtained for the BCT ceramics poled at 100 °C with 30 kV/cm field for 20 min. The aging behavior of the piezoelectric property is also investigated.