Characterization of a soldering system consisting of a glass from the system CaOAl2O3B2O3SiO2 and wollastonite

In this work, the characterization of a soldering system with wollastonite as filler added as powder to the powdered base glass is shown. A soldering system consisting of the base glass and a coexisting crystalline phase is created which is then pressed to pellets and sintered to maximum density. Wollastonite increases the thermal expansion coefficient of the base glass after sintering the samples. In the present paper, the sintering behavior of the soldering system and possible interactions between glass and filler are analyzed. Also, density and porosity after sintering and the resulting crystalline phases are characterized. The mixtures with wollastonite contents up to 30% showed suitable sintering behavior and good density (low porosity). From 40% wollastonite on, the sintering of the samples was not satisfying and porosity was still high after sintering. The main crystalline phases were anorthite, wollastonite and pseudowollastonite, which occurred in all samples. This shows that all three phases are coexisting phases of the glass composition.