Influence of curing condition and precracking time on the self-healing behavior of Engineered Cementitious Composites

This paper investigates the self-healing behavior of Engineered Cementitious Composites (ECC) with focus on the influence of curing condition and precracking time. Four-point bending tests were used to precrack ECC beams at different age, followed by different curing conditions, including air curing, 3% CO2 concentration curing, cyclic wet/dry (dry under 3% CO2 concentration) curing and water curing. For all curing conditions, deflection capacity after self-healing can recover or even exceed that from virgin samples with almost all precracking ages. After self-healing, flexural stiffness was also retained significantly compared with that from virgin samples, even though the level of retaining decreases with the increase of precracking time. The flexural strength increases for samples pre-cracked at the age of 14 days and 28 days, presumably due to continuous hydration of cementitious materials afterwards. Furthermore, it is promising to utilize nanoclay as distributed internal water reservoirs to promote self-healing behavior within ECC without relying on external water supply.